作者：肖存杰 王腾蛟 刘洪林 汪南平 常家文 陈 茜
单位：海军医学研究所，上海市 200433
关键词：潜艇；隔声密封材料；定性定量分析；卫生学评价
海军医学杂志990108 摘要 目的：评价G-39型隔声密封材料能否用于核潜艇舱室。方法：对该材料的高温热解释放物和常温释放物进行定性定量分析及卫生学评价。定性分析用色谱-质谱联用仪及比色法，定量分析用气相色谱法及比色法。结果：定性分析出21种气体，通过90d(40℃)定量分析，苯、甲苯、总烃、一氧化碳、二氧化碳、苯酚均低于核潜艇舱室空气组分容许浓度(GJB11-84)。结论：G-39型隔声密封材料可用于核潜艇。
Measurement of Gases Released by Type G-39 Sound Isolating and Se aling Material Used aboard Submarines and Its Medical Evaluation
, http://www.100md.com
Xiao Cunjie, Wang Tengjiao, Liu Honglin, et al.
Naval Medical Research Institute, Shanghai 200433
Abstract Purpose:The study was carried out to evaluate whether type G-39 sound-insulating and sealing material can be used aboard submarines.Methods:Quan titative and qualitative analysis, and medical evaluation were made on the substances released at high temperature and room temperature. Qualitative analysis was made by using gaschromatography-mass spectrometry and chromatography, while quantita tive analysis was done by using gas chromatography and chromatometry. Results: 21 gases were identified quantitatively. Quantitative analysis (at 40℃) for 90 days proved that concentrations of ben zene, toluene, total-hydrocarbon, CO2, CO and phenol were all lower than the maximum allowable limits for atmospheric components in submarine compartments (GJB 11-84).Conclusion: G-39 can be us ed aboard submarines.
, http://www.100md.com
Key words submarine; soundisol ating and sealing material; quantitative and qualitative analysis; medical evaluation
G-39型隔声密封材料系化工部青岛海洋涂料研究所研制，由海军医学研究所对该材料进 行高温热解产物及常温释放气体定性定量分析，并对能否用于核潜艇舱室作出卫生学评价。根据该材料与潜艇的实际用量比，进行了高温热解气体的定性和90d常温(40℃)定量分析。
1 材料与方法
1.1 受试材料 G-39型隔声密封材料。
1.2 试验条件
1.2.1 常温定性分析 将受试材料置于玻璃烧瓶内，在45℃烘箱内恒温2h，取其瓶内气体定性分析。
, http://www.100md.com
1.2.2 高温定性分析 将受试材料切割成小块，置于玻璃烧瓶内，煤气火焰加热至600～700℃，取瓶内热解气体作定性分析。
1.2.3 定量分析 根据该材料与潜艇的实际用量比，将0.01m2试验材料密封于0.2m3、40℃的恒温试验箱内，定期取箱内气体的作90d定量分析。
1.3 测试方法
1.3.1 定性分析用JMS-D300色谱/质谱/计算机联用仪。色谱柱为OV-01玻璃毛细管柱(50m×0.25mm)，由40℃程序升温至220℃。质谱离子源为电子轰击源，电子能量70eV，离子化电流300μA，源温度180℃。
1.3.2 定量分析分别用GJC-20K、103和102型气相色谱仪。色谱柱分别为聚四氟乙烯管柱，内装固定相分别为chromosorb10160～80目(1m×Φ2mm)、玻璃珠20～40目(3.2m×Φ3mm)、TDX-0160～80目(3.5m×Φ3mm)；柱温分别为120℃、110℃和80℃。
, 百拇医药
2 结 果
该材料在高温(600～700℃)热解及常温(45℃)主要释放气体见表1。该材料在恒温箱内通过90d定期分析常温(40℃)条件下主要释放气体浓度及卫生标准见表2。
表1 G-39型隔声密封材料释放的气体 温度(℃)
释 放 气 体
45
苯、甲苯、总烃、一氧化碳、二氧化碳、苯酚
600～700
苯、甲苯、苯酚、丙烯、1-丁烯、正丁烷、1-戊烯、正戊烷、乙基环丙烷、环戊烷、1-己烯、正己烷、1，3环戊二烯、1-庚烯、正庚烷、1-辛烯、正辛烷、1-壬烯、正壬烷、一氧化碳、二氧化碳
, 百拇医药
表2 G-39型隔声密封材料释放气体浓度及卫生标准 名 称
90d密封期浓度(μmol/mol)
卫生标准(μmol/mol)
5
10
15
20
30
40
50
60
70
, 百拇医药
80
90
核潜艇
工业
苯
0.04
0.04
0.04
0.04
0.04
0.04
0.04
0.04
, http://www.100md.com
0.03
0.03
0.03
1.0
12.5
甲苯
0.21
0.16
0.15
0.15
0.14
0.10
0.10
, 百拇医药
0.09
0.07
0.05
0.04
2.7
26.5
总烃
/
0.15
0.25
0.40
0.75
0.50
, http://www.100md.com
0.40
0.50
0.50
0.40
0.30
10.0
86.0
一氧化碳
/
/
/
/
/
, http://www.100md.com
/
/
/
/
/
/
15.0
26.0
二氧化碳*
0.05
0.07
0.07
0.06
, 百拇医药
0.06
0.06
0.06
0.07
0.05
0.06
0.06
0.8
0.5
苯酚
[]
1.3
*：浓度单位为%； /：为未检出； []：为未制定标准
, http://www.100md.com
3 讨 论
该材料释放气体定性分析出21种，有芳烃、酚、烯烃、脂肪烃、无机化合物共5种类型。毒性较大的有苯、甲苯、一氧化碳和二氧化碳，其它为低毒或无毒。定量检测出的6种气体中，苯的毒性最大，其急性毒性作用主要作用于中枢神经系统，慢性主要作用于造血组织及神经系统。甲苯可引起一般不适症状与轻度中枢神经系统症状。一氧化碳随呼吸气进入血液循环后，与Hb和其它某些含铁蛋白(如肌红蛋白、细胞色素等)形成不可逆性结合，使机体遭受缺氧血症。二氧化碳可引起呼吸加深加快现象，头痛、头昏、耳鸣、恶心、智力机能抑制、意识不清、感觉丧失、昏迷。总烃为麻醉性毒物，主要使中枢神经系统机能紊乱。但通过90d定量分析常温(40℃)条件下6种气体检出的浓度，除苯酚未检出外，5种气体均低于核潜艇舱室空气组分容许浓度标准(GJB11-84)，不致于引起上述中毒症状。
该材料定性检测出21种气体组分，定量检测中只检测出5种气体，其它气体未检出，可能与该材料在配比中溶剂比例大小有关，或是释放出的浓度很低，低于仪器的检测下限，以致于未检出其它气体。
4 结 论
由结果可见，G-39型隔声密封材料在40℃按潜艇实际用量比密封90d期间其释放气体一氧化碳、二氧化碳、苯、甲苯、总烃、苯酚均低于核潜艇舱室空气组分容许浓度(GJB11-84)和工业标准，其余成分未检出，故该材料可用于核潜艇舱室。
(收稿：1999-06-01), http://www.100md.com
单位：海军医学研究所，上海市 200433
关键词：潜艇；隔声密封材料；定性定量分析；卫生学评价
海军医学杂志990108 摘要 目的：评价G-39型隔声密封材料能否用于核潜艇舱室。方法：对该材料的高温热解释放物和常温释放物进行定性定量分析及卫生学评价。定性分析用色谱-质谱联用仪及比色法，定量分析用气相色谱法及比色法。结果：定性分析出21种气体，通过90d(40℃)定量分析，苯、甲苯、总烃、一氧化碳、二氧化碳、苯酚均低于核潜艇舱室空气组分容许浓度(GJB11-84)。结论：G-39型隔声密封材料可用于核潜艇。
Measurement of Gases Released by Type G-39 Sound Isolating and Se aling Material Used aboard Submarines and Its Medical Evaluation
, http://www.100md.com
Xiao Cunjie, Wang Tengjiao, Liu Honglin, et al.
Naval Medical Research Institute, Shanghai 200433
Abstract Purpose:The study was carried out to evaluate whether type G-39 sound-insulating and sealing material can be used aboard submarines.Methods:Quan titative and qualitative analysis, and medical evaluation were made on the substances released at high temperature and room temperature. Qualitative analysis was made by using gaschromatography-mass spectrometry and chromatography, while quantita tive analysis was done by using gas chromatography and chromatometry. Results: 21 gases were identified quantitatively. Quantitative analysis (at 40℃) for 90 days proved that concentrations of ben zene, toluene, total-hydrocarbon, CO2, CO and phenol were all lower than the maximum allowable limits for atmospheric components in submarine compartments (GJB 11-84).Conclusion: G-39 can be us ed aboard submarines.
, http://www.100md.com
Key words submarine; soundisol ating and sealing material; quantitative and qualitative analysis; medical evaluation
G-39型隔声密封材料系化工部青岛海洋涂料研究所研制，由海军医学研究所对该材料进 行高温热解产物及常温释放气体定性定量分析，并对能否用于核潜艇舱室作出卫生学评价。根据该材料与潜艇的实际用量比，进行了高温热解气体的定性和90d常温(40℃)定量分析。
1 材料与方法
1.1 受试材料 G-39型隔声密封材料。
1.2 试验条件
1.2.1 常温定性分析 将受试材料置于玻璃烧瓶内，在45℃烘箱内恒温2h，取其瓶内气体定性分析。
, http://www.100md.com
1.2.2 高温定性分析 将受试材料切割成小块，置于玻璃烧瓶内，煤气火焰加热至600～700℃，取瓶内热解气体作定性分析。
1.2.3 定量分析 根据该材料与潜艇的实际用量比，将0.01m2试验材料密封于0.2m3、40℃的恒温试验箱内，定期取箱内气体的作90d定量分析。
1.3 测试方法
1.3.1 定性分析用JMS-D300色谱/质谱/计算机联用仪。色谱柱为OV-01玻璃毛细管柱(50m×0.25mm)，由40℃程序升温至220℃。质谱离子源为电子轰击源，电子能量70eV，离子化电流300μA，源温度180℃。
1.3.2 定量分析分别用GJC-20K、103和102型气相色谱仪。色谱柱分别为聚四氟乙烯管柱，内装固定相分别为chromosorb10160～80目(1m×Φ2mm)、玻璃珠20～40目(3.2m×Φ3mm)、TDX-0160～80目(3.5m×Φ3mm)；柱温分别为120℃、110℃和80℃。
, 百拇医药
2 结 果
该材料在高温(600～700℃)热解及常温(45℃)主要释放气体见表1。该材料在恒温箱内通过90d定期分析常温(40℃)条件下主要释放气体浓度及卫生标准见表2。
表1 G-39型隔声密封材料释放的气体 温度(℃)
释 放 气 体
45
苯、甲苯、总烃、一氧化碳、二氧化碳、苯酚
600～700
苯、甲苯、苯酚、丙烯、1-丁烯、正丁烷、1-戊烯、正戊烷、乙基环丙烷、环戊烷、1-己烯、正己烷、1，3环戊二烯、1-庚烯、正庚烷、1-辛烯、正辛烷、1-壬烯、正壬烷、一氧化碳、二氧化碳
, 百拇医药
表2 G-39型隔声密封材料释放气体浓度及卫生标准 名 称
90d密封期浓度(μmol/mol)
卫生标准(μmol/mol)
5
10
15
20
30
40
50
60
70
, 百拇医药
80
90
核潜艇
工业
苯
0.04
0.04
0.04
0.04
0.04
0.04
0.04
0.04
, http://www.100md.com
0.03
0.03
0.03
1.0
12.5
甲苯
0.21
0.16
0.15
0.15
0.14
0.10
0.10
, 百拇医药
0.09
0.07
0.05
0.04
2.7
26.5
总烃
/
0.15
0.25
0.40
0.75
0.50
, http://www.100md.com
0.40
0.50
0.50
0.40
0.30
10.0
86.0
一氧化碳
/
/
/
/
/
, http://www.100md.com
/
/
/
/
/
/
15.0
26.0
二氧化碳*
0.05
0.07
0.07
0.06
, 百拇医药
0.06
0.06
0.06
0.07
0.05
0.06
0.06
0.8
0.5
苯酚
[]
1.3
*：浓度单位为%； /：为未检出； []：为未制定标准
, http://www.100md.com
3 讨 论
该材料释放气体定性分析出21种，有芳烃、酚、烯烃、脂肪烃、无机化合物共5种类型。毒性较大的有苯、甲苯、一氧化碳和二氧化碳，其它为低毒或无毒。定量检测出的6种气体中，苯的毒性最大，其急性毒性作用主要作用于中枢神经系统，慢性主要作用于造血组织及神经系统。甲苯可引起一般不适症状与轻度中枢神经系统症状。一氧化碳随呼吸气进入血液循环后，与Hb和其它某些含铁蛋白(如肌红蛋白、细胞色素等)形成不可逆性结合，使机体遭受缺氧血症。二氧化碳可引起呼吸加深加快现象，头痛、头昏、耳鸣、恶心、智力机能抑制、意识不清、感觉丧失、昏迷。总烃为麻醉性毒物，主要使中枢神经系统机能紊乱。但通过90d定量分析常温(40℃)条件下6种气体检出的浓度，除苯酚未检出外，5种气体均低于核潜艇舱室空气组分容许浓度标准(GJB11-84)，不致于引起上述中毒症状。
该材料定性检测出21种气体组分，定量检测中只检测出5种气体，其它气体未检出，可能与该材料在配比中溶剂比例大小有关，或是释放出的浓度很低，低于仪器的检测下限，以致于未检出其它气体。
4 结 论
由结果可见，G-39型隔声密封材料在40℃按潜艇实际用量比密封90d期间其释放气体一氧化碳、二氧化碳、苯、甲苯、总烃、苯酚均低于核潜艇舱室空气组分容许浓度(GJB11-84)和工业标准，其余成分未检出，故该材料可用于核潜艇舱室。
(收稿：1999-06-01), http://www.100md.com