口内环境中对澳丝机械性能衰减的研究(1)
摘 要：目的 探究澳丝在口内环境中使用一段时间后，对其机械性能及表面形貌的影响。为临床上寻找合理的更换时机提供参考。方法 选择0.014英寸、0.016英寸两种不同型号的澳丝，分别在口内使用1～5个月。使用后回收作为样本，分别检测其机械性能及表面形貌并与新弓丝进行比较。结果 0.014、0.016英寸两种尺寸的澳丝在口腔中使用长达5个月后其弹性较新丝相比，差异无统计学意义(P>0.05)。但扫描电镜显示，澳丝在口内使用状态下，随着使用时间的延长，其表面发生了明显的腐蚀现象。结论 在口内使用长达5个月的时间内澳丝可以保持良好的弹性，但随着使用时间增长，弓丝表面变得粗糙。
关键词：澳丝；弹性；表面形貌
中图分类号：R783.5 文献标识码：A DOI：10.3969/j.issn.1006-1959.2018.09.038
文章编号：1006-1959(2018)09-0123-03
, 百拇医药
Abstract：Objective To explore the effect of Australian silk on its mechanical properties and surface topography after a period of time in oral environment.It provides reference for finding reasonable replacement time in clinic.Methods Choose 0.014 inches and 0.016 inches of two different types of Australian silk，respectively，for 1～5 months in mouth.After recycling，the mechanical properties and surface morphology of the samples were measured and compared with the new archwires.Results There was no significant difference in elasticity between two Australian wires of 0.014 and 0.016 inches after being used in oral cavity for up to 5 months compared with that of new silk(P>0.05).But scanning electron microscope showed that the surface of Australian silk was corroded obviously with the prolongation of time.Conclusion Australia silk can maintain good elasticity after oral use for 5 months，but the surface of arch silk becomes rough with the increase of service time.
, 百拇医药
Key words：Australian silk；Elasticity；Surface morphology
近年来，错颌畸形的患病率明显增高[1]。伴随着固定矫治器在世界范围内被广泛用于错颌畸形的治疗，矫治弓丝作为固定矫治最重要的组成部分之一，得到越来越多学者的广泛重视和研究[2]。40年代初wikock公司研制出了高强度不锈钢丝，被称为澳大利亚特种不锈钢丝，简称澳丝。它的特点是屈服点高，可以较长时间保持初始力值，较硬但弹性很好。腐蚀现象不仅会影响美观和卫生的维护，也会影响弓丝的性能，增加医生对合适矫治力的判断难度[3]。因此，正确的理解口内使用过程中腐蚀对弓丝的影响是合理运用矫治力以产生最适合的生理性牙齿移动的必然要求。本实验主要探究的是澳丝在口腔应用条件下其弹性及表面形貌的时效变化，以便临床中更好的掌握更换时机。
1材料与方法
1.1材料选取 同一种品牌的澳丝(wikock公司生产)用于佳木斯大学口腔医学院及泰山医学院正畸门诊患者，矫治过程中选用0.022英寸的不锈钢标准方丝弓托槽，并用不锈钢结扎丝结扎弓丝。在定期复诊患者中，选用新的原始的0.014、0.016英寸两种标准尺寸的澳丝，并于使用第1～5个月后回收各10根以用作研究，回收后立刻用蒸馏水冲洗弓丝上的松散残渣，并将弓丝放入塑料密封袋中进行保存。选取患者的标准是相似的年龄间隔和错牙合类型。回收弓丝时是应记录以下变量：①患者姓名；②放置弓丝的日期；③弓丝横截面和放置时的弓形；④弓丝移除日期。
, 百拇医药
1.2方法
1.2.1弹力测试 选用佳木斯大学微机控制电子万能实验机(Model No. WDW-10E； Serial No.192， Made in China P.R.)进行实验。将每一弓丝一端均于尖牙处截断，获得尖牙远端相对平直的区域。每组弓丝各截取十根，获得样本量n=10。以三点弯曲实验检测矫正牙弓丝的变形程度(应变)与弓丝产生的力量(应力)之间的关系及其差异大小。参考美国正畸弓丝ISO标准(15841：2006)，实验在室温即(23±2)℃下進行，本实验弓丝两端呈自由状态，两端支持体间跨距为10 mm，连接杆的加卸载速度为5 mm/min，压头置于弓丝中点使弓丝挠曲变形，将加载力0 N作为挠曲位移的起始点。弓丝最大挠曲量为2 mm。通过三点弯曲试验软件，将每个样本获得的载荷-位移曲线显示于试验机相连的计算机上。比较得出随着使用时间的延长弓丝弹性的的变化，三点弯曲实验测力装置，见图1。, 百拇医药(张雪楠 郑嵘 吴立鹏)
关键词：澳丝；弹性；表面形貌
中图分类号：R783.5 文献标识码：A DOI：10.3969/j.issn.1006-1959.2018.09.038
文章编号：1006-1959(2018)09-0123-03
, 百拇医药
Abstract：Objective To explore the effect of Australian silk on its mechanical properties and surface topography after a period of time in oral environment.It provides reference for finding reasonable replacement time in clinic.Methods Choose 0.014 inches and 0.016 inches of two different types of Australian silk，respectively，for 1～5 months in mouth.After recycling，the mechanical properties and surface morphology of the samples were measured and compared with the new archwires.Results There was no significant difference in elasticity between two Australian wires of 0.014 and 0.016 inches after being used in oral cavity for up to 5 months compared with that of new silk(P>0.05).But scanning electron microscope showed that the surface of Australian silk was corroded obviously with the prolongation of time.Conclusion Australia silk can maintain good elasticity after oral use for 5 months，but the surface of arch silk becomes rough with the increase of service time.
, 百拇医药
Key words：Australian silk；Elasticity；Surface morphology
近年来，错颌畸形的患病率明显增高[1]。伴随着固定矫治器在世界范围内被广泛用于错颌畸形的治疗，矫治弓丝作为固定矫治最重要的组成部分之一，得到越来越多学者的广泛重视和研究[2]。40年代初wikock公司研制出了高强度不锈钢丝，被称为澳大利亚特种不锈钢丝，简称澳丝。它的特点是屈服点高，可以较长时间保持初始力值，较硬但弹性很好。腐蚀现象不仅会影响美观和卫生的维护，也会影响弓丝的性能，增加医生对合适矫治力的判断难度[3]。因此，正确的理解口内使用过程中腐蚀对弓丝的影响是合理运用矫治力以产生最适合的生理性牙齿移动的必然要求。本实验主要探究的是澳丝在口腔应用条件下其弹性及表面形貌的时效变化，以便临床中更好的掌握更换时机。
1材料与方法
1.1材料选取 同一种品牌的澳丝(wikock公司生产)用于佳木斯大学口腔医学院及泰山医学院正畸门诊患者，矫治过程中选用0.022英寸的不锈钢标准方丝弓托槽，并用不锈钢结扎丝结扎弓丝。在定期复诊患者中，选用新的原始的0.014、0.016英寸两种标准尺寸的澳丝，并于使用第1～5个月后回收各10根以用作研究，回收后立刻用蒸馏水冲洗弓丝上的松散残渣，并将弓丝放入塑料密封袋中进行保存。选取患者的标准是相似的年龄间隔和错牙合类型。回收弓丝时是应记录以下变量：①患者姓名；②放置弓丝的日期；③弓丝横截面和放置时的弓形；④弓丝移除日期。
, 百拇医药
1.2方法
1.2.1弹力测试 选用佳木斯大学微机控制电子万能实验机(Model No. WDW-10E； Serial No.192， Made in China P.R.)进行实验。将每一弓丝一端均于尖牙处截断，获得尖牙远端相对平直的区域。每组弓丝各截取十根，获得样本量n=10。以三点弯曲实验检测矫正牙弓丝的变形程度(应变)与弓丝产生的力量(应力)之间的关系及其差异大小。参考美国正畸弓丝ISO标准(15841：2006)，实验在室温即(23±2)℃下進行，本实验弓丝两端呈自由状态，两端支持体间跨距为10 mm，连接杆的加卸载速度为5 mm/min，压头置于弓丝中点使弓丝挠曲变形，将加载力0 N作为挠曲位移的起始点。弓丝最大挠曲量为2 mm。通过三点弯曲试验软件，将每个样本获得的载荷-位移曲线显示于试验机相连的计算机上。比较得出随着使用时间的延长弓丝弹性的的变化，三点弯曲实验测力装置，见图1。, 百拇医药(张雪楠 郑嵘 吴立鹏)